Effect of polyvinyl alcohol and carboxymethylcellulose on the technological properties of fish gelatin films

Mar 14, 2023

Scientific Reports volume 12, Article number: 10497 (2022) Cite this article

1426 Accesses

3 Citations

1 Altmetric

Metrics details

The objective of this work was to develop biodegradable films by mixing gelatin/carboxymethylcellulose (FG/CMC) and gelatin/polyvinyl alcohol (FG/PVOH) and to evaluate the effect of adding these polymers on the properties of fish gelatin films. The films FG/CMC and FG/PVOH were produced in the proportions 90/10, 80/20 and 70/30 and characterized their physical, chemical and functional properties. The addition of CMC and PVOH improved the mechanical strength, barrier property and water solubility of gelatin films. FG/CMC films showed greater tensile strength and greater solubility than FG/PVOH. The maximum concentration of CMC promoted the highest mechanical resistance, while the highest PVOH content produced the film with the lowest solubility. The proposed mixing systems proved to be adequate to improve the properties of fish gelatin films, with potential for application in the packaging sector.

New technologies and the demands of the current world, as well as the large consumption of processed foods that require packaging (primary, secondary and tertiary), have caused an increase in the generation of solid waste, which remains for hundreds and/or thousands of years in the environment, causing an environmental crisis, as well as economic and social problems1. Given this, there has been growing concern about the fate of plastic packaging derived from oil due to the serious environmental problems and ecological risks that can already be observed2,3.

Biodegradable film packages are thin layers previously formed as plastic films, which are generally produced through the casting technique or extrusion and are used to wrap foods4. The biodegradable films produced from biopolymers have an essential role in reducing the environmental impact caused by the disposal of non-biodegradable plastic residues5, once they present potential for reducing, or substituting petroleum-based plastics. Such biological-based films must offer all the necessary functions of containment, protection, preservation and information, in an economical and environmentally friendly way6.

As an alternative to films produced with conventional materials, many studies have been performed using biodegradable, non-toxic, biocompatible and renewable sources to develop films that do not pollute the environment7. Among these sources, gelatin, an animal protein resulting from the partial hydrolysis of collagen8, stands out as a promising raw material for developing biodegradable food packaging, due to excellent characteristics such as formation of films and light and oxygen barrier properties9.

Fish gelatin extracted from processing residues, such as bones and skins is a potential alternative to mammals, due to the socio-cultural and health aspects involved in obtaining bovine and porcine sources10. In addition, the use of waste for the development of biodegradable films has important benefits for the fishing industry and the environment11. Although gelatin films have appropriate characteristics for film making12, the hydrophilic nature of this material can limit its use13. Gelatin films have lower mechanical resistance and low water resistance when compared to conventional plastics, being one of the main disadvantages for its use as packaging material.

Much research is being carried out in order to improve the functional properties of these films11, including mixing with other polymers is an alternative to make the properties of gelatin films more efficient. The mixture of polymers, such as proteins/polysaccharides and/or synthetic/natural polymers, makes it possible to obtain composite films, resulting in materials with better properties than pure components. The physical and chemical properties of the films can be improved, enabling numerous applications, resulting in good performance in the final product6.

Carboxymethylcellulose (CMC) is an anionic cellulose derivative produced through an etherification reaction, by partially replacing hydroxyl groups of cellulose with carboxymethyl. The food, medicine and textile industries have great interest in this polymer due to its biodegradability, biocompatibility, availability, non-toxicity and good mechanical and barrier properties, in addition to presenting favorable characteristics to form films14,15.

Polyvinyl alcohol (PVOH) is a synthetic polymer that is also important in the packaging area16, of high polarity17,18, low cost, non-toxic and biodegradable19, being produced commercially by hydrolysis of acetate of polyvinyl20. This material has received great attention due to its excellent oxygen barrier properties, mechanical properties, chemical resistance, film-forming capacity, water solubility, mechanical properties and biocompatibility21,22. CMC and PVOH have been widely used in polymer blends to produce new polymeric materials with improved characteristics22,23,24,25.

Developing films from the mixture of gelatin (FG) with other polymers such as carboxymethylcellulose and/or polyvinyl alcohol is a viable alternative for the use of residues generated by the fishing industry, reducing the environmental impact, and at the same time making the properties of more functional gelatin films, increasing their potential use as biodegradable packaging. Therefore, the objective of this work was to produce biodegradable films by mixing gelatin/carboxymethylcellulose (FG/CMC) and gelatin/polyvinyl alcohol (FG/PVOH) and to evaluate the effect of adding these polymers on the properties of fish gelatin films.

Fish gelatin, the main component of the film formulations, was extracted from yellow hake skin (Cynoscion acoupa), donated by Indústria de Pesca, Ecomar Ltda (Vigia, PA, Brazil). Sodium chloride (NaCl) (Exodus Cientifica, Sumaré, SP, Brazil), Sodium hydroxide (NaOH) (Exodus Cientifica, Hortolândia, SP, Brazil), Acetic acid (C2H4O2) (Cinética, Itapevi, SP, Brazil), Sodium Salt Carboxymethylcellulose—CAS 9004-32-4 (Neon, Suzano, SP, Brazil), Polyvinyl Alcohol HD = 89.5% hydrolyzed—CAS 9002-89-5 (Exodus Cientifica, Sumaré, SP, Brazil) and Glycerol—CAS 56-81-5 (Isofar, Rio de Janeiro, RJ, Brazil) were purchased from local businesses.

The extraction of fish gelatin was carried out according to the methodology described by26. The skins were cut into 4 cm × 4 cm, washed in running water and immersed in 0.6 M sodium chloride (NaCl)—CAS 7647-14-5 solutions for 15 min, 0.3 M sodium hydroxide (NaOH)—CAS 1310-73-2 for 15 min and lastly in acetic acid (C2H4O2)—CAS 1189-52-3 0.02 M for 60 min, in the proportion 1:5 (weight/volume). All stages occurred under agitation (85 rpm at 25 °C), with the skin washed in water, with 3 repetitions. Subsequently, the skins were placed in a water bath (Tecnal, Te-057, Brazil) at 60 °C for 6 h to extract the gelatin, and the material obtained was filtered through faillet fabric. Then, the obtained solution was placed in stainless steel trays for drying in an oven (Tecnal, Te-394/3, Brazil) at 50 °C for 16 h. Finally, the gelatin was vacuum packed (Fastvac Wrapping Machine, F200, Brazil) and stored at − 22 °C until the films were made.

The films were produced by casting. The films were made from mixtures of polymeric solutions FG/CMC and FG/PVOH in the proportions 90/10, 80/20 and 70/30, with a total concentration of 3% (m/v) of solution and 10% (m/m polymers) of plasticizer.

The filmogenic solutions were prepared separately, dissolving gelatin (G), carboxymethylcellulose (CMC) and polyvinyl alcohol (PVOH) in distilled water. To prepare the gelatin filmogenic solution (FG), glycerol was added as a plasticizer and heated in a water bath (Tecnal, TE-057, Brazil) at 70 °C for 15 min. The CMC and PVOH solutions were heated to 70 and 90 °C, respectively, for a period of 60 min, and then mixed with the FG solution.

The FG/CMC filmogenic solutions were placed on a shaking plate (Quimis, Q-221.1, Brasil) and the FG/PVOH were stirred in a homogenizer (Ultra Stirrer-380, Brazil), both for 30 min. Finally, they were placed on a silicone support (22 cm in diameter × 3 cm in height) and dried in an oven (Tecnal, Te-394/3, Brazil) at 30 °C for approximately 15 h. The films obtained were vacuum packed and kept at room temperature. A control film (FG) was also made without the addition of CMC and PVOH.

The thickness was determined using a digital micrometer with a resolution of 0.001 mm (Insize Co., modelo IP54, São Paulo, SP, Brasil). Eight random locations were selected around each film obeying a 60 mm edge spacing.

To determine the tensile strength and percentage of elongation at the break of the films, texture analyzer equipment (Stable Micro Systems, model TA. XT-Plus, England) was used, according to the standard method ASTM D882-9127, in which the initial separation of the grips and the probe speed were of 20 mm and 1 mm s−1, respectively. The films were cut into pieces of 60 mm × 25 mm (length × width) and the tensile strength (TS) and the elongation percentage (% E) were calculated by Eqs. (1) and (2), respectively. The analysis was performed in triplicate.

where TS: tensile strength (MPa); Fm: maximum force when the film breaks (N); A: cross-sectional area of the film (m2); E: elongation (%); dT: total distance at the moment of rupture (mm); d initial: initial separation distance of the claws (50 mm).

The water vapor permeability (WVP) of the films was measured by the modified ASTM D882-95 method, described by28. The samples were sealed with silicon adhesive (Orbi Química Co., Leme, SP, Brazil) in the circular opening of a glass permeation container of 4.5 × 7.0 cm (inside diameter × height) containing 10 g of silica gel (0% 0% RH; 0 Pa of water vapor pressure at 30 °C). These containers were placed in desiccators containing distilled water at 30 °C (99% RH; 4244.9 Pa of water vapor pressure at 30 °C). They were weighed at 1 h intervals for a period of 10 h. WVP was calculated from Eq. (3) and the analysis was performed in triplicate.

where WVP: water vapor permeability (gm m−2 S−1 Pa−1); W: weight gain from the desiccant (g); X: film thickness (m); A: surface area of the exposed biofilm (m2) t: incubation time (hours); ∆P: partial pressure difference (Pa).

To determine solubility, the films were cut into 2 cm diameter discs and placed in an oven at 105 °C for 24 h and weighed. Subsequently, immersed in containers containing 50 ml of water and shaken in a refrigerated Shaker incubator (Lucadema, model LUCA-223) with a speed of 150 rpm for a period of 24 h at 25 °C. Finally, the samples were dried (105 °C for 24 h), to determine the dry matter not dissolved in water29. The analysis was performed in triplicate.

The instrumental color of the samples was determined with a portable colorimeter (model CR 400, Konica Minolta Co., Chiyoda , Tokyo, Japan), obtaining parameters of L* (brightness), a* (intensity of red), b* (intensity of yellow) and the total color difference (ΔE*) was calculated according to Eq. (4), in relation to the control film (FG).

where Δ is the difference of the color parameters of the biofilm sample in relation to the white standard (L: 95.59; a: − 5.56; b: 8.16).

Opacity was analyzed using a spectrophotometer (DU 640, Bachman, USA), at a wavelength of 600 nm and absorbance was measured. The opacity of the films was calculated using Eq. (5), according to the method described by30.

where O = opacity; Abs600 = absorbance at 600 nm and x = film thickness (mm).

To obtain the micrographs, the samples were fixed on supports with double-sided adhesive tape, metallized with gold, at an approximate thickness of 15 nm (Emitech, model K550X, England), with a covering time of 1.5 min. The cross-sectional images of the films were obtained using a scanning electron microscope (Zeiss, model EVO-MA-10, Germany) at a constant acceleration voltage of 10 kV and magnification of 500×, with an acceleration voltage of 10 kV, electron beam current of 100 µA and a working distance of 8.5 mm.

The thermogravimetric curves were obtained using a TGA-50 Shimadzu, Japan analyzer, according to31. The samples were submitted to a heating rate of 10 °C/min, in an atmosphere of nitrogen at 50 ml/min) in the temperature range of 25–600 °C.

FTIR analyzes were performed using an Agilent spectrometer, model Cary 630 using the Total Attenuated Reflectance technique in the range of 650–4000 cm−1, with 4 cm−1 resolution and accumulation of 32 scans.

X-ray diffraction (XRD) measurements were performed on a Siemens D5000 X-ray diffractometer with Cu-Kα radiation (λ = 1.78901 nm) accelerated in voltage and current of 40 kV and 40 mA, respectively. The XRD pattern was collected in the scan range 2θ of 5°–80° at a step size of 0.02°/min.

The analysis results were subjected to analysis of variance (ANOVA) and Tukey test (p < 0.05), analyzed using the Statistica® version 7.0 program32.

The results showed a difference (p < 0.05) between the thickness values (Fig. 1a), and the films with CMC and PVOH showed greater thickness when compared to the control (FG). This can be attributed to changes in the microstructure due to interactions between polymers33. The results indicate that this parameter is related to the type of polymer added (CMC and PVOH), regardless of the concentration used.

Means and standard deviations (SD) of the following properties: (a) Thickness; (b) Tensile strength (TS); (c) Elongation (% E); (d) Water vapor permeability (WVP); (e) Solubility of FG films, 90FG/10CMC, 80FG/20CMC; 70FG/30CMC; 90FG/10PVOH, 80FG/20PVOH, 70FG/30PVOH. Different letters represent significantly different values (p < 0.05).

The control (FG) showed low tensile strength, which is characteristic of films made with fish gelatin, which restricts its use as food packaging34. The amount of CMC added to the film matrix increased (p < 0.05) the TS values, making the films more resistant compared to gelatin (FG), however, with reduced elongation (% E) (Fig. 1b). The maximum TS value was obtained with 30% of CMC in the mixture, in contrast this same composition revealed the lowest % E. A similar behavior to the one found in this study was observed by35 when assessing protein-polysaccharide films.

This behavior may be due to the interactions between gelatin and CMC, which made the film more resistant, suggesting increased structural cohesion of the films. Such characteristic is related to the ability of the polymer to form strong and numerous bonds between two polymeric chains, making their rupture more difficult when subjected to mechanical forces36. And the increase in structural cohesion causes a reduction in the flexibility of the film and, consequently, in the percentage of % E37. According to38, the mechanical characteristics of the mixing film depend on the intermolecular forces between the polymer chains and the molecular symmetry of each polymer.

Besides the interactions between polymers, the excellent mechanical strength of CMC gelatin films can be partially explained in terms of their semi-crystalline structure35, once the greater the crystallinity, the greater the resistance to traction compared to the amorphous structure, because the crystallinity reduces the degree of freedom for the mobility of the molecules39.

FG/PVOH films showed greater tensile strength than the control film, as it was added and/or increased the proportion of PVOH in the mixture. However, lower than TS of CMC films. A similar phenomenon has been reported by other researchers40,41. Regarding elongation, PVOH is a polymer capable of producing highly extensible films, as described by42,43.

According to44, the occurrence of intermolecular interactions between polymers significantly improves the tensile strength, due to the formation of inter and intramolecular hydrogen bonds. PVOH has good mechanical properties due to its flexible C–C bonds and the presence of a large number of OH groups in their chains45. In the presence of several hydroxyl groups, PVOH is able to act as a plasticizer, increasing the molecule free volume and mobility and, consequently, making the polymeric matrix less dense, thus improving flexibility46. In this study, the increase in %E of the FG/PVOH films possibly occurred because the incorporation of PVOH into the polymeric matrix reduces the number of interactions between the protein chains of the gelatin, and promotes bonds between them and other PVOH chains through hydrogen bonds47, as shown in the FT-IR results.

In general, the incorporation of CMC as well as PVOH in gelatin films positively influenced the mechanical properties, making the films more resistant and flexible.

The composite films FG/CMC and FG/PVOH showed lower permeability to water vapor in all studied concentrations (p < 0.05) when compared to the control (Fig. 1c). The reduction in WVP in films with CMC may be due to the strong intermolecular interaction between the chains of proteins and polysaccharides, such as hydrogen, hydrophobic and electrostatic bonds48, reducing the space free and intermolecular distance in the matrix, making diffusion of water molecules more difficult49. The highly crystalline and hydrophobic character of cellulose fibers may also have affected the film's WVP. The incorporation can produce a tortuous path, blocking the passage of water molecules through the film matrix50.

As for the composite FG/PVOH films, the addition of polyvinyl alcohol allowed the OH groups of this polymer to interact with the gelatin chains by intermolecular forces such as hydrogen bonds, reducing the number of hydrophilic groups. The strong interactions between the polymer chains in the films reduce the permeation of water vapor molecules through the structural matrix, reducing the WVP values41. In addition, the more ordered molecular structure of PVOH, as well as a greater number of OH groups, reflect an increase in the polarity and crystallinity of FG/PVOH composite films.

The concentrations of CMC and PVOH studied did not influence the WVP of the films, nor did the type of polymer affect the interaction of the films with water (p > 0.05). The WVP values found for the studied composite films are in accordance with the results presented previously performed with polymer mixtures51,52,53.

The solubility of the FG control film was the highest (Fig. 1d) and similar to the value (64%) reported by54 for fish skin gelatin films. The high solubility of these films is a limitation to replace the use of conventional plastics, especially for applications such as packaging, due to the hydrophilic character of the proteins (presence of polar peptides) and the relevant content of hydrophilic plasticizer (glycerol) added to give elasticity to the film34.

The addition of CMC and PVOH significantly reduced (p < 0.05) the solubility of the films. The concentrations of CMC used are adequate to provide the entanglement of the gelatin polypeptide chains with the added polymers. This interference can provide a significant blockage of the gelatin's ability to interact with water molecules35.

In FG/PVOH films, the reduction in solubility may be due to the formation of hydrogen bonds between gelatin and PVOH molecules, which decreased the amount of hydroxyl groups available, making it difficult to associate the polymer with water molecules33. The results indicated that the combination of polymers improves the integrity and water resistance of gelatin films, an important property for the use of the material as a biodegradable packaging for foods with high humidity.

Color and opacity can directly affect the appearance of food and consumer satisfaction, therefore, they are important packaging properties55. The color tests showed that the addition of CMC and PVOH influenced the color parameters L*, a*, b* (Fig. 2a–c).

Means and standard deviations (SD) of the color parameters: (a) L*; (b) a*; (c) b*, (d) ΔE and (e) opacity of the FG, 90FG/10CMC, 80FG/20CMC; 70FG/30CMC; 90FG/10PVOH, 80FG/20PVOH, and 70FG/30PVOH films. Different letters represent significantly different values (p < 0.05).

For all films analyzed, the values of a* are negative, indicating the presence of a green component, while parameter b* is positive with a tendency to yellow. For FG/CMC films, there was a reduction in the values of L* and a* and an increase in b* (p < 0.05), when compared to the control film, that is, they reflect less light. The FG/PVOH mixture had a similar behavior regarding the values of L* and b*, however the parameter a* showed higher values. As the values of a* and b* were close to zero, it is considered that the films presented a slightly gray color. The total color difference values ΔE were not affected by the amount and type of polymer added.

The biodegradable films produced, including FG and the FG/CMC and FG/PVOH mixtures can be observed in Fig. 3. The influence of CMC and PVOH concentrations added to filmogenic solutions was observed in the L* parameter of the films, with a significant decrease. This behavior can be explained by the compaction of the filmogenic matrix, due to the reduction of the spacing between the polymer chains, reducing the passage of light through the film56, confirmed by the opacity results, which showed less transparency with the addition of polymers. Result similar to that obtained by57 in gelatin films with increasing concentrations of agar. The transparency values observed in this study in all composite films are lower than those reported for low density polyethylene (4.26 A600/mm), which is a widely commercialized synthetic plastic58.

Biodegradable films: (a) FG; (b) 90FG/10CMC; (c) 80FG/20CMC; (d) 70FG/30CMC; (e) 90FG/10PVOH; (f) 80FG/20PVOH, (g) 70FG/30PVOH.

The FTIR spectra of the FG control films and the FG/CMC and FG/PVOH compounds are shown in Fig. 4. The FG spectrum showed characteristic bands of gelatin in approximately 3274 cm−1 (amide A, representative of the elongation of the NH– bond coupled to the hydrogen bond); 2922 cm−1 (due to the elongation of H); 1639 cm−1 (amide I, representative of C=O, hydrogen bond coupled to COO); 1534 cm−1 (amide II, representative of the flexion of NH groups coupled to CN elongation) and 1244 cm−1 (amide III, representative of the vibrations in the CN and NH bond plane of vibrations of the bound amide or groups of glycine CH2)59,60. The band located at 1041 cm−1 also corresponds to glycerol (group –OH) added as a plasticizer.

FT-IR spectra of FG film and FG/CMC and FG/PVOH mixtures.

Analyzing the FG/CMC spectra, it was possible to observe that after the addition of CMC, some peaks were shifted to new frequencies. For example, the amide I peak was shifted from 1639 (FG film) to 1630 cm−1 in composite films in all studied proportions. Amide I is normally used to analyze the secondary structure of proteins61. The decrease in the wave numbers of this band may suggest the occurrence of structural changes in protein chains, such as in the helical structure of gelatin62. Meanwhile, the peak of amide II was changed from 1534 to 1525 cm−1 (90FG/10CMC) and 1524 cm−1 (80FG/20CMC; 70FG/30CMC), and that of 1244 amide III to 1234 cm−1. The changes in the spectra suggested the presence of protein-polysaccharide interactions via hydrogen bonding49. In addition, the peak 3274 cm−1, corresponding to the band amide A, was displaced by 3267 cm−1, due to the occurrence of hydrogen bonds between gelatin and CMC. The new intermolecular changes formed can result in a denser structure in the films33.

Regarding the FG/PVOH film, variations in the absorption in the region of amides I, II and III were observed when PVOH was incorporated in different proportions in the gelatin, indicating the establishment of chemical bonds. It was observed that in these films the peak referring to amide I, located at 1639 cm−1 was slightly shifted to 1631 cm−1, regardless of the polymer concentration. The band amide I is the most sensitive of the gelatin, and such behavior suggests the occurrence of interactions through hydrogen bonds between the gelatin carbonyl group and the PVOH hydroxyl group, increasing intermolecular forces, which may, in a way, indicate the occurrence of crystallinity in the films produced63. The presence of PVOH also influenced the amide II band, causing a displacement from 1534 to 1529 cm−1, as well as affecting the characteristic signs of the amide III band, which was changed from 1242 to 1192 cm−1. It was also identified the change in the peaks related to amide A, which were moved to higher frequencies with the increase in the proportion of PVOH. For these mixtures, the peaks located in the 3500–3200 cm−1 region refer to the stretching vibration of the inter and intramolecular hydrogen bonds, which indicates the presence of hydrogen bonds between gelatin and PVOH.

The TGA analysis evaluated the effect of adding CMC and PVOH on the thermal stability of the gelatin-based films and the TGA and DTGA curves are shown in Fig. 5. The FG and FG/PVOH films showed three stages of weight loss, while the FG/CMC mixtures showed only two stages. In the first stage, all films showed a loss of mass of 6–8.5% in the temperature range of 30–130 °C. This stage is associated with the loss of free and absorbed water64.

TGA and DTGA thermograms of the control film (FG) and mixing films: (a) FG; (b) 90FG/10CMC; (c) 80FG/20CMC; (d) 70FG/30CMC; (e) 90FG/10PVOH; (f) 80FG/20PVOH; (g) 70FG/30PVOH.

In the control film (FG), the second stage occurred between 225 and 265 °C, with a loss of mass around 5%, probably associated with low molecular weight protein fractions and the plasticizer65. And in the third stage, a loss of mass of about 34% was observed at 275–345 °C, being attributed to the thermal degradation of peptide bonds in the main chain of gelatin66.

FG/CMC films, in the second stage, showed weight loss of approximately 37% at 240–345 °C, probably due to protein and polysaccharide degradation. Therefore, it is possible to notice that the addition of CMC did not influence the thermal resistance of the films, which remained stable compared to the pure gelatin films.

The FG/PVOH films, in the second stage, showed mass loss of 14–16% at 180–250 °C, while the third stage was observed at 275–360 °C with weight loss between 26 and 29%. The reduction in the initial degradation temperature of these films compared to FG/CMC reveals that the molecular interactions between gelatin and PVOH affected the thermal behavior of the films, indicated by the decrease in thermal stability.

XRD analysis was performed to check for a possible change in crystallinity of gelatin films when adding other polymers to this matrix (Fig. 6). The XRD pattern of the FG film showed two diffraction peaks, at 2θ = 7°–8°, attributed to the presence of a small amount of triple helical structure, characteristic of collagen, accompanied by the wide diffraction peak at 2θ = 21° which corresponds to the amorphous halo of the protein67.

(a) XRD pattern of FG/CMC and FG films and (b) FG/PVOH and FG films.

It can be seen in Fig. 6a that all FG/CMC films presented XRD profiles similar to FG, however, with greater intensity, indicating that CMC was well dispersed in the gelatin matrix. The increase in peak intensity was the result of interactions between polymers, through intermolecular hydrogen bonds between gelatin and CMC, producing more ordered structures, indicating an increase in crystallinity in the film matrix. Increase in peak intensities was also observed by33 in gelatin films and epigallocatechin gallate.

The diffractograms shown in Fig. 6b demonstrated that the different proportions of PVOH produced films with typical characteristics of semicrystalline material. In porcine gelatin and PVOH films, other authors68 obtained a semicrystalline diffraction peak around at a 2θ = 20°, similar to what was observed in this work. Similar patterns of XRD, too, have been observed in studies by69 in pure PVOH films. According to42, PVOH has a flexible structure, which allows the packaging of molecules and crystallization, while gelatin crystallizes due to its tendency to resaturation61.

The microstructure of the films was evaluated to verify the influence of the addition of CMC and PVOH on the structure of the films (Fig. 7). The transversal images of the FG film have a more homogeneous structure, while FG/CMC showed imperfections, which may be due to the presence of different macromolecules in the polymeric matrix and to the interactions between these components70. It is observed that the microstructures of the composite films FG/CMC and FG/PVOH are more uniform as the concentration of polymers increases, producing more compact and dense structures, which may have better mechanical and barrier properties. This structure may be due to intermolecular polymer associations or compatibility between components71.

Cross-sectional images of the FG film and FG/CMC, FG/PVOH mixtures in different proportions.

The 70FG/30CMC mixture was identified as the most homogeneous of the studied proportions, confirmed by the greater mechanical resistance found for this composition. On the other hand, the presence of some roughness was more noticeable in the structure of the films with PVOH, being in accordance with the mechanical results, which indicated higher values of tensile strength for FG/CMC. However, no evidence of phase separation was observed in any of the composite films, demonstrating the compatibility of both polymer mixtures.

The physical, chemical and functional properties of FG films were modified by the addition of CMC and PVOH. It was found that the incorporation of 10% of CMC or PVOH was sufficient to produce films with better mechanical resistance, water vapor barrier and water solubility properties, in relation to gelatin film.

FG/CMC films showed greater mechanical resistance, but were more sensitive to water than FG/PVOH. The SEM analysis suggested compatibility between the components of the films. The 70FG/30CMC film showed greater tensile strength, while the 70FG/30PVOH obtained less solubility in water.

The results indicated that the polymeric mixtures studied in this work are adequate to improve the functional properties of fish gelatin films. What can expand the possibilities of making films with potential application in the packaging sector, with the advantage of biodegradability and low production cost, with the use of waste and the consequent reduction of environmental impact.

The datasets generated and/or analyzed during the current study are available from the corresponding author on reasonable request.

Landim, A. P. M. et al. Sustainability concerning food packaging in Brazil. Polymer 26, 82–92. https://doi.org/10.1590/0104-1428.1897 (2016).

Article Google Scholar

Weng, W. & Wu, F. Water resistance and mechanical property improvement of tilapia (Tilapia zillii) scale gelatin films by dehydrated thermal treatment. J. Food Sci. Technol. 52, 3358–3366. https://doi.org/10.1007/s13197-014-1401-z (2014).

Article CAS PubMed PubMed Central Google Scholar

Herrera, N., Salaberria, A. M., Mathew, A. P. & Oksman, K. Plasticized polylactic acid nanocomposite films with cellulose and chitin nanocrystals prepared using extrusion and compression molding with two cooling rates: Effects on mechanical, thermal and optical properties. Compos. Part. A Appl. Sci. Manuf. 83, 89–97. https://doi.org/10.1016/j.compositesa.2015.05.024 (2016).

Article CAS Google Scholar

Silva-Weiss, A. et al. Natural additives in bioactive edible films and coatings: Functionality and applications in foods. Food Eng. Rev. 5, 200–216. https://doi.org/10.1007/s12393-013-9072-5 (2013).

Article CAS Google Scholar

Soo, P. Y. & Sarbon, N. M. Preparation and characterization of edible chicken skin gelatin film incorporated with rice flour. Food Packag. Shelf Life 15, 1–8. https://doi.org/10.1016/j.fpsl.2017.12.009 (2018).

Article Google Scholar

Nur Hanani, Z. A., Roos, Y. H. & Kerry, Y. H. Use and application of gelatin as potential biodegradable packaging materials for food products. Int. J. Biol. Macromol. 71, 94–102. https://doi.org/10.1016/j.ijbiomac.2014.04.027 (2014).

Article CAS PubMed Google Scholar

Hassan, B., Chatha, S. A. A., Hussain, A. I., Zia, K. M. & Akhtar, N. Recent advances on polysaccharides, lipids and protein based edible films and coatings: A review. Int. J. Biol. Macromol. 109, 1095–1107. https://doi.org/10.1016/j.ijbiomac.2017.11.097 (2018).

Article CAS PubMed Google Scholar

Ramos, M., Valdés, A., Beltrán, A. & Garrigós, M. Gelatin-based films and coatings for food packaging applications. Coatings 6, 41–61. https://doi.org/10.3390/coatings6040041 (2016).

Article CAS Google Scholar

Etxabide, A., Uranga, J., Guerrero, P. & De La Caba, K. Development of active gelatin films by means of valorisation of food processing waste: A review. Food Hydrocoll. 68, 192–198. https://doi.org/10.1016/j.foodhyd.2016.08.021 (2017).

Article CAS Google Scholar

Gómez-guillén, M. C., Gimenéz, B., López-Caballero, M. E. & Montero, M. P. Functional and bioactive properties of collagen and gelatin from alternative sources: A review. Food Hydrocoll. 25, 1813–1827. https://doi.org/10.1016/j.foodhyd.2011.02.007 (2011).

Article CAS Google Scholar

Hosseini, S. F. & Gómez-Guillén, M. C. A state-of-the-art review on the elaboration of fish gelatin as bioactive packaging: Special emphasis on nanotechnology-based approaches. Trends Food. Sci. Technol. 79, 125–135. https://doi.org/10.1016/J.TIFS.2018.07.022 (2018).

Article CAS Google Scholar

Gómez-guillén, M. C., Ihl, M., Bifani, V. & Silva, A. Montero P edible films made from tuna-fish gelatin with antioxidant extracts of two different murta ecotypes leaves (Ugni molinae Turcz). Food Hydrocoll. 21, 1133–1143. https://doi.org/10.1016/j.foodhyd.2006.08.006 (2007).

Article CAS Google Scholar

Battisti, R. et al. Gelatin-coated paper with antimicrobial and antioxidant effect for beef packaging. Food Packag. Shelf Life 11, 115–124. https://doi.org/10.1016/j.fpsl.2017.01.009 (2017).

Article MathSciNet Google Scholar

Tongdeesoontorn, W., Mauer, L. J., Wongruong, S., Sriburi, P. & Rachtanapun, P. Effect of carboxymethyl cellulose concentration on physical properties of biodegradable cassava starch-based films. Chem. Cent. J. 5, 1–8. https://doi.org/10.1186/1752-153x-5-6 (2014).

Article Google Scholar

Oun, A. A. & Rhim, J. W. Preparation of multifunctional carboxymethyl cellulose-based films incorporated with chitin nanocrystal and grapefruit seed extract. Int. J. Biol. Macromol. https://doi.org/10.1016/j.ijbiomac.2019.10.191 (2019).

Article PubMed Google Scholar

Chen, C. H., Wang, F. Y., Mao, C. F., Liao, W. T. & Hsieh, C. D. Studies of chitosan: II. Preparation and characterization of chitosan/poly (vinyl alcohol)/gelatin ternary blend films. Int. J. Biol. Macromol. 43, 37–42. https://doi.org/10.1016/j.ijbiomac.2007.09.005 (2008).

Article CAS PubMed Google Scholar

Pal, K., Banthia, A. K. & Majumdar, D. K. Preparation and characterization of poly (vinyl alcohol) e gelatin hydrogel membranes for biomedical applications. AAPS PharmSciTech 8, 1–5. https://doi.org/10.1208/pt080121 (2007).

Article Google Scholar

Siddaiaha, T. et al. Structural, optical and thermal characterizations of PVA/MAA: EA polyblend films. Mater. Res. 21, 1–10. https://doi.org/10.1590/1980-5373-MR-2017-0987 (2018).

Article Google Scholar

Aloui, H. et al. Synergistic effect of halloysite and cellulose nanocrystals on the functional properties of PVA based nanocomposites. ACS Sustain. Chem. Eng. 4, 794–800. https://doi.org/10.1021/acssuschemeng.5b00806 (2016).

Article CAS Google Scholar

Halima, B. N. Poly(vinyl alcohol): Review of its promising applications and insights into biodegradation. RSC Adv. 6, 39823–39832. https://doi.org/10.1039/C6RA05742J (2016).

Article ADS Google Scholar

Liu, D. et al. Effect of oxidation degrees of graphene oxide on the structure and properties of poly (vinyl alcohol) composite films. Compos. Sci. Technol. 129, 146–152. https://doi.org/10.1016/j.compscitech.2016.04.004 (2016).

Article CAS Google Scholar

Ma, Q., Liang, T., Cao, L. & Wang, L. Intelligent poly (vinyl alcohol)-chitosan nanoparticles-mulberry extracts films capable of monitoring pH variations. Int. J. Biol. Macromol. 108, 576–584. https://doi.org/10.1016/j.ijbiomac.2017.12.049 (2018).

Article CAS PubMed Google Scholar

El-Sayed, S., Mahmoud, K., Fatah, A. & Hassen, A. DSC, TGA and dielectric properties of carboxymethyl cellulose/polyvinyl alcohol blends. Physica B Condens. Matter 406, 4068–4076. https://doi.org/10.1016/j.physb.2011.07.050 (2011).

Article ADS CAS Google Scholar

Nur Hazirah, M. A. S. P., Isa, M. I. N. & Sarbon, N. M. Effect of xanthan gum on the physical and mechanical properties of gelatin-carboxymethyl cellulose film blends. Food Packag. Shelf Life 9, 55–63. https://doi.org/10.1016/j.fpsl.2016.05.008 (2016).

Article Google Scholar

Morsi, M., Rajeh, A. & Menazea, A. Nanosecond laser-irradiation assisted the improvement of structural, optical and thermal properties of polyvinyl pyrrolidone/carboxymethyl cellulose blend filled with gold nanoparticles. J. Mater. Sci. Mater. Electron. 30, 2693–2705. https://doi.org/10.1007/s10854-018-0545-4 (2019).

Article CAS Google Scholar

Silva, E. V. C., Lourenço, L. F. H. & Pena, R. S. Optimization and characterization of gelatin from kumakuma (Brachyplatystoma filamentosum) skin. CyTA J. Food 15, 361–368. https://doi.org/10.1080/19476337.2016.1266391 (2017).

Article CAS Google Scholar

American Society for Testing and Materials – ASTM. D882-91. Standard Test Methods for Tensile Properties of Thin Plastic Sheeting (Annual Book of ASTM Standards, 1996).

Google Scholar

Arfat, Y. A., Benjakul, S., Prodpran, T. & Osako, K. Development and characterization of blend films on fish protein isolate and fish gelatin. Food Hydrocoll. 39, 58–67. https://doi.org/10.1016/j.foodhyd.2013.12.028 (2014).

Article CAS Google Scholar

Gontard, N., Duchez, C., Cuq, J. & Guilbert, S. Edible composite films of wheat gluten and lipids: Water vapor permeability and other physical properties. Int. J. Food Sci. Technol. 29(1994), 39–50. https://doi.org/10.1111/j.1365-2621.1994.tb02045.x (1994).

Article CAS Google Scholar

Gontard, N. & Guilbert, S. Biopackaging: Technology and properties of edible and/or biodegradable material of agricultural origin. In Food packaging and preservation (ed. Mathlouthi, M.) (Blackie Academic and Professional, 1994).

Google Scholar

Nuthong, P., Benjakul, S. & Prodpran, T. Characterization of porcine plasma protein-based films as affected by pretreatment and cross-linking agents. Int. J. Biol. Macromol. 44, 143–148. https://doi.org/10.1016/j.ijbiomac.2008.11.006 (2009).

Article CAS PubMed Google Scholar

STATSOFT. Statistica for Windows, versão 7.0 (2004).

Liu, J. et al. Preparation and characterization of active and intelligent films based on fish gelatin and haskap berries (Lonicera caerulea L.) extract. Food Packag. Shelf Life 22, 100417. https://doi.org/10.1016/j.ijbiomac.2019.05.029 (2019).

Article CAS Google Scholar

Hosseini, S. F., Javidi, Z. & Rezaei, M. Efficient gas barrier properties of multi-layer films based on poly (lactic acid) and fish gelatin. Int. J. Biol. Macromol. 92, 1205–1214. https://doi.org/10.1016/j.ijbiomac.2016.08.034 (2016).

Article CAS PubMed Google Scholar

Setareh, Rezaei, M. M. & Hosseini, S. F. Physico-chemical and microstructural properties of fish gelatin/agar bio-based blend films. Carbohydr. Polym. 157, 784–793. https://doi.org/10.1016/j.carbpol.2016.10.061 (2017).

Article CAS Google Scholar

Gontard, N. & Guilbert, S. Bio-packaging: Technology and properties of edible and/or biodegradable material of agricultural origin. Boletim SBCTA 30, 3–15 (1996).

Google Scholar

Kester, J. J. & Fennema, O. R. Edible films and coatings: A review. Food Technol. 12, 47–59 (1986).

Google Scholar

Suyatma, N. E., Copinet, A., Tighzert, L. & Coma, V. Mechanical and barrier properties of biodegradable films made from chitosan and poly (lactic acid) blends. J Polym. Environ. 12, 1–6. https://doi.org/10.1023/B:JOOE.0000003121.12800.4e (2004).

Article CAS Google Scholar

Rubin, I. I. Injection molding of thermoplastics. In SPI Plastics Engineering Handbook of the Society of the Plastics Industry (ed. Berings, M. L.) 133–178 (Springer, 1991).

Chapter Google Scholar

Chai, W. L., Chow, J. D., Chen, C. C., Chuang, F. S. & Lu, W. C. Evaluation of the biodegradability of polyvinyl alcohol/starch blends: A methodological comparison of environmentally friendly materials. J. Polym. Environ. 17, 71–82. https://doi.org/10.1007/s10924-009-0123-1 (2009).

Article CAS Google Scholar

Gómez-Aldapa, C. A., Velazquez, G., Gutierrez, M. C., Rangel-Vargas, E. & Aguirre-Loredo, R. Y. Effect of polyvinyl alcohol on the physicochemical properties of biodegradable starch films. Mater. Chem. Phys. 239, 122027. https://doi.org/10.1016/J.MATCHEMPHYS.2019.122027 (2020).

Article Google Scholar

Xiao, C., Liu, H., Gao, S. & Zhang, L. Characterization of poly(vinyl alcohol)-konjac glucomannan blend films. J. Macromol. Sci. A 37, 1009–1021. https://doi.org/10.1081/MA-100101137 (2000).

Article Google Scholar

Sudhamani, S. R., Prasad, E. M. & Sankar, K. U. DSC and FTIR studies on gellan and polyvinyl alcohol (PVA) blend films. Food Hydrocoll. 17, 245–250. https://doi.org/10.1016/S0268-005X(02)00057-7 (2003).

Article CAS Google Scholar

Chambi, H. N. M. & Grosso, C. R. F. Mechanical and water vapor permeability properties of biodegradables films based on methylcellulose, glucomannan, pectin and gelatin. Food Sci. Technol. 31, 739–746. https://doi.org/10.1590/S0101-20612011000300029 (2011).

Article Google Scholar

Tian, H., Yan, J., Rajulu, A. V., Xiang, A. & Luo, X. Fabrication and properties of polyvinyl alcohol/starch blend films: Effect of composition and humidity. Int. J. Biol. Macromol. 96, 518–523. https://doi.org/10.1016/j.ijbiomac.2016.12.067 (2017).

Article CAS PubMed Google Scholar

Musso, Y. S., Salgado, P. R. & Mauri, A. N. Smart gelatin films prepared using red cabbage (Brassica oleracea L.) extracts as solvent. Food Hydrocoll. 89, 674–681. https://doi.org/10.1016/j.foodhyd.2018.11.036 (2019).

Article CAS Google Scholar

Guimarães, M. Jr., Botaro, V. R., Novack, K. M., Teixeira, F. G. & TonolI, G. H. D. Strain-induced crystallization of natural rubber/zinc dimethacrylate composites studied using synchrotron X-ray diffraction and molecular simulation. J. Polym. Res. 22, 1–18. https://doi.org/10.1007/s10965-015-0834-z (2015).

Article CAS Google Scholar

Guerrero, P., Kerry, J. P. & De La Caba, K. FTIR characterization of protein–polysaccharide interactions in extruded blends. Carbohydr. Polym. 111, 598–605. https://doi.org/10.1016/j.carbpol.2014.05.005 (2014).

Article CAS PubMed Google Scholar

Mohajer, S., Rezaei, M. & Hosseini, S. F. Physico-chemical and microstructural properties of fish gelatin/agar bio-based blend films. Carbohydr. Polym. 157, 784–793. https://doi.org/10.1016/j.carbpol.2016.10.061 (2017).

Article CAS PubMed Google Scholar

Kristo, E. & Biliaderis, G. C. Physical properties of starch nanocrystal-reinforced pullulan films. Carbohydr. Polym. 29, 254–259. https://doi.org/10.1016/j.carbpol.2006.07.021 (2007).

Article CAS Google Scholar

Ma, X., Chang, P. R. & Yu, J. Properties of biodegradable thermoplastic pea starch/carboxymethyl cellulose and pea starch/microcrystalline cellulose composites. Carbohydr. Polym. 72, 369–375. https://doi.org/10.1016/j.carbpol.2007.09.002 (2008).

Article CAS Google Scholar

Fama, L., Gerschenson, L. & Goyanes, S. Starch-vegetable fibre composites to protect food products. Carbohydr. Polym. 75, 230–235. https://doi.org/10.1016/j.carbpol.2008.06.018 (2009).

Article CAS Google Scholar

Ghanbarzadeh, B., Almasi, H. & Entezami, A. Physical properties of edible modified starch/carboxymethyl cellulose films. Innov. Food Sci. Emerg. Technol. 11, 697–702. https://doi.org/10.1016/j.ifset.2010.06.001 (2010).

Article CAS Google Scholar

Hosseini, S. F., Rezaei, M. & Ghavi, F. F. Preparation and functional properties of fish gelatin–chitosan blend edible films. Food Chem. 136, 1490–14951. https://doi.org/10.1016/j.foodchem.2012.09.081 (2013).

Article CAS Google Scholar

Zhang, Z. J. et al. Preparation and characterization of biocomposite chitosan film containing Perilla frutescens (L.) Britt. essential oil. Ind. Crops. Prod. 112, 660–667. https://doi.org/10.1016/j.indcrop.2017.12.073 (2018).

Article CAS Google Scholar

Yang, L., Paulson, A. T. & Nickerson, M. T. Mechanical and physical properties of calcium-treated gellan films. Food Res. Int. 43, 1439–2144. https://doi.org/10.1016/j.foodres.2010.04.010 (2010).

Article CAS Google Scholar

Jridi, M., Abdelhedi, O., Zouari, N., Fakhfakh, N. & Nasri, M. Development and characterization of grey triggerfish gelatin/agar bilayer and blend films containing vine leaves bioactive compounds. Food Hydrocoll. 89, 370–378. https://doi.org/10.1016/j.foodhyd.2018.10.039 (2019).

Article CAS Google Scholar

Guerrero, P., Nur Hanani, Z. A., Kerry, J. P. & De La Caba, K. Characterization of soy protein-based films prepared with acids and oils by compression. J. Food. Eng. 107, 41–49. https://doi.org/10.1016/j.jfoodeng.2011.06.003 (2011).

Article CAS Google Scholar

Tongnuanchan, P., Benjakul, S. & Prodpran, T. Structural, morphological and thermal behaviour characterisations of fish gelatin film incorporated with basil and citronella essential oils as affected by surfactants. Food Hydrocoll. 41, 33–43. https://doi.org/10.1016/j.foodhyd.2014.03.015 (2014).

Article CAS Google Scholar

Nilsuwan, K., Benjakul, S. & Prodpran, T. Properties, microstructure and heat seal ability of bilayer films based on fish gelatin and emulsified gelatin films. Food Biophys. 12, 234–243. https://doi.org/10.1007/s11483-017-9479-2 (2017).

Article Google Scholar

Yakimets, I. et al. Mechanical properties with respect to water content of gelatin films in glassy state. Polymer 46, 12577–12585. https://doi.org/10.1016/j.polymer.2005.10.090 (2005).

Article CAS Google Scholar

Theerawitayaart, W., Prodpran, T. & Benjakul, S. Properties of films from fish gelatin prepared by molecular modification and direct addition of oxidized linoleic acid. Food Hydrocoll. 88, 291–300. https://doi.org/10.1016/j.foodhyd.2018.10.022 (2019).

Article CAS Google Scholar

Moraes, I. C. et al. Influence of the degree of hydrolysis of poly(vinyl alcohol) on the physical properties of films based on blends of gelatin and poly(vinyl alcohol) plasticized with glycerol. Food Sci. Technol. 28, 738–745. https://doi.org/10.1590/S0101-20612008000300034 (2008).

Article Google Scholar

Hoque, M. S., Benjakul, S. & Prodpran, T. Properties of film from cuttlefish (Sepia pharaonis) skin gelatin incorporated with cinnamon, clove and star anise extracts. Food Hydrocoll. 25, 1085–1097. https://doi.org/10.1016/j.foodhyd.2010.10.005 (2011).

Article CAS Google Scholar

Kanmani, P. & Rhim, J. W. Physical, mechanical and antimicrobial properties of gelatin based active nanocomposite films containing AgNPs and nanoclay. Food Hydrocoll. 35, 644–652. https://doi.org/10.1016/j.foodhyd.2013.08.011 (2014).

Article CAS Google Scholar

Martucci, J. F. & Ruseckaite, R. A. Biodegradation behavior of three-layer sheets based on gelatin and poly (lactic acid) buried under indoor soil conditions. Polym. Degrad. Stab. 116, 36–44. https://doi.org/10.1016/j.polymdegradstab.2015.03.005 (2015).

Article CAS Google Scholar

Benbettaïeb, T., Karbowiak, C. H. & Brachais, F. D. Impact of electron beam irradiation on fish gelatin film properties. Food Chem. 195, 11–18. https://doi.org/10.1016/j.foodchem.2015.03.034 (2016).

Article CAS PubMed Google Scholar

Maria, T. M. C., Carvalho, R. A., Sobral, J. A., Habitante, A. M. B. Q. & Solorza-Feria, J. The effect of the degree of hydrolysis of the PVA and the plasticizer concentration on the color, opacity, and thermal and mechanical properties of films based on PVA and gelatin blends. J. Food Eng. 87, 191–199. https://doi.org/10.1016/j.jfoodeng.2007.11.026 (2008).

Article CAS Google Scholar

Kaczmarek, H. & Podgórski, A. The effect of UV-irradiation on poly (vinyl alcohol) composites with montmorillonite. J. Photochem. Photobiol. A 191, 209–215. https://doi.org/10.1016/j.jphotochem.2007.04.025 (2007).

Article CAS Google Scholar

Bilanovic, D., Starosvetsky, J. & Armon, R. H. Preparation of biodegradable xanthan–glycerol hydrogel, foam, film, aerogel and xerogel at room temperature. Carbohydr. Polym. 148, 243–250. https://doi.org/10.1016/j.carbpol.2016.04.058 (2016).

Article CAS PubMed Google Scholar

Tian, H., Xu, G., Yang, B. & Guo, G. Microstructure and mechanical properties of soy protein/agar blend films: Effect of composition and processing methods. J. Food Eng. 107, 21–26. https://doi.org/10.1016/j.jfoodeng.2011.06.008 (2011).

Article CAS Google Scholar

Download references

The authors would like to thank the Coordination for the Improvement of Higher Education Personnel (CAPES) for granting a Master's scholarship to the first author, the National Council for Scientific and Technological Development (CNPq) and the Dean of Research and Graduate Studies (PROPESP) for funding this research.

Animal Research Laboratory - LAPOA, Graduate Program in Food Science and Technology - PPGCTA, Federal University of Pará - UFPA, Belém, PA, Brazil

Gleyca de Jesus Costa Fernandes & Lúcia de Fátima Henriques Lourenço

Department of Food Technology, Federal University of Vicosa, Av. PH Rolfs, s/n, Vicosa, MG, 36570-900, Brazil

Pedro Henrique Campelo

Food Science Department, Federal University of Lavras, Lavras, MG, 37200-000, Brazil

Jayne de Abreu Figueiredo & Hugo Junior Barbosa de Souza

Pará Federal Institute of Education, Science and Technology - IFPA, Castanhal, PA, Brazil

Maria Regina Sarkis Peixoto Joele

Chemical Department, Federal University of Minas Gerais, Belo Horizonte, MG, Brazil

Maria Irene Yoshida

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

G.J.C.F.: Conceptualization, validation, formal analysi, investigation, visualization writing—review and editing, investigation. P.H.C.: Conceptualization. J.A.F.: Resources. H.J.B.S.: conceptualization, resources and editing. M.R.S.P.J.: Conceptualization, resources. M.I.Y.: Resources. L.F.H.L.: Conceptualization, supervision, project administration. All authors reviewed the manuscript.

Correspondence to Gleyca de Jesus Costa Fernandes.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Fernandes, G.d.C., Campelo, P.H., de Abreu Figueiredo, J. et al. Effect of polyvinyl alcohol and carboxymethylcellulose on the technological properties of fish gelatin films. Sci Rep 12, 10497 (2022). https://doi.org/10.1038/s41598-022-14258-y

Download citation

Received: 25 February 2022

Accepted: 03 June 2022

Published: 21 June 2022

DOI: https://doi.org/10.1038/s41598-022-14258-y

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

Journal of Packaging Technology and Research (2022)

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.